常用不锈钢紧固件材料化学成分
奥氏体不锈钢化学成分（GB/T3098.6、GB/T3098.15、GB/T3098.16、GB/T3098.21)
| ISO代号 | 化学成分（质量分数）a / % | 对应的紧固件组别b | |||||||||||
| C | Si | Mn | P | S | Cr | Mo | Ni | Cu | N | Nb | Ti | ||
| 奥氏体不锈钢 | |||||||||||||
| 4305-303-00-I | 0.12 | 1 | 2 | 0.06 | ≥0.15 | 17.0~19.0 | / | 8.0~10.0 | 1 | 0.1 | / | / | A1 |
| 4301-304-00-I | 0.07 | 1 | 2 | 0.045 | 0.03 | 17.5~19.5 | / | 8.0~10.5 | / | 0.1 | / | / | A2 |
| 4307-304-03-I | 0.03 | 1 | 2 | 0.045 | 0.03 | 17.5~19.5 | / | 8.0~10.5 | / | 0.1 | / | / | A2L |
| 4311-304-53-I | 0.03 | 1 | 2 | 0.045 | 0.03 | 17.5~19.5 | / | 8.0~11.0 | / | 0.12~0.22 | / | / | A2L |
| 4567-304-98-X | 0.08 | 1 | 2 | 0.045 | 0.03 | 17.0~19.0 | / | 8.0~10.5 | 1.0~3.0 | / | / | / | A2 |
| 4567-304-30-I | 0.04 | 1 | 2 | 0.045 | 0.03 | 17.0~19.0 | / | 8.0~10.5 | 3.0~4.0 | 0.1 | / | / | A3 |
| 4541-321-00-I | 0.08 | 1 | 2 | 0.045 | 0.03 | 17.0~19.0 | / | 9.0~12.0 | / | / | / | 5×C~0.70 | A3 |
| 4550-347-00-I | 0.08 | 1 | 2 | 0.045 | 0.03 | 17.0~19.0 | / | 9.0~12.0 | / | / | 10×C~1.00 | / | A3 |
| 4401-316-00-I | 0.08 | 1 | 2 | 0.045 | 0.03 | 16.0~18.0 | 2.00~3.00 | 10.0~13.0 | / | 0.1 | / | / | A4 |
| 4404-316-03-I | 0.03 | 1 | 2 | 0.045 | 0.03 | 16.5~18.5 | 2.00~3.00 | 10.0~13.0 | / | 0.1 | / | / | A4L |
| 4406-316-53-I | 0.03 | 1 | 2 | 0.045 | 0.03 | 16.5~18.5 | 2.00~3.00 | 10.0~12.5 | / | 0.12~0.22 | / | / | A4L |
| 4578-316-76-E | 0.04 | 1 | 2 | 0.045 | 0.015 | 16.5~17.5 | 2.00~2.50 | 10.0~11.0 | 3.0~3.5 | 0.1 | / | / | A4 |
| 4571-316-35-I | 0.08 | 1 | 2 | 0.045 | 0.03 | 16.5~18.5 | 2.00~2.50 | 10.5~13.5 | / | / | / | 5×C~0.70 | A5 |
| 4529-089-26-I | 0.02 | 0.75 | 2 | 0.035 | 0.015 | 19.0~21.0 | 6.0~7.0 | 24.0~26.0 | 0.5~1.5 | 0.15~0.25 | / | / | A8 |
| 4547-312-54-I | 0.02 | 0.7 | 1 | 0.035 | 0.015 | 19.5~20.5 | 6.0~7.0 | 17.5~18.5 | 0.50~1.00 | 0.18~0.25 | / | / | A8 |
| 4478-083-67-U | 0.03 | 1 | 2 | 0.04 | 0.03 | 20.0~22.0 | 6.0~7.0 | 23.5~25.5 | 0.75 | 0.18~0.25 | / | / | A8 |
马氏体、铁素体和双相钢化学成分（ GB/T3098.6、GB/T3098.15、GB/T3098.16、GB/T3098.21)
| ISO代号 | 化学成分（质量分数）a / % | 对应的紧固件组别b | |||||||||||
| C | Si | Mn | P | S | Cr | Mo | Ni | Cu | N | Nb | Ti | ||
| 马氏体不锈钢 | |||||||||||||
| 4006-410-00-I | 0.08~0.15 | 1 | 1.5 | 0.04 | 0.03 | 11.5~13.5 | / | 0.75 | / | / | / | / | C1 |
| 4021-420-00-I | 0.16~0.25 | 1 | 1.5 | 0.04 | 0.03 | 12.0~14.0 | / | / | / | / | / | / | C1 |
| 4028-420-00-I | 0.26~0.35 | 1 | 1.5 | 0.04 | 0.03 | 12.0~14.0 | / | / | / | / | / | / | C1 |
| 4057-431-00-X | 0.12~0.22 | 1 | 1.5 | 0.04 | 0.03 | 15.0~17.0 | / | 1.50~2.50 | / | / | / | / | C3 |
| 4005-416-00-I | 0.08~0.15 | 1 | 1.5 | 0.04 | ≥0.15 | 12.0~14.0 | 0.6 | / | / | / | / | / | C4 |
| 铁素体不锈钢 | |||||||||||||
| 4016-430-00-I | 0.08 | 1 | 1 | 0.04 | 0.03 | 16.0~18.0 | / | / | / | / | / | / | F1 |
| 双相不锈钢 | |||||||||||||
| 4482-320-01-X | 0.03 | 1 | 4.0~6.0 | 0.035 | 0.03 | 19.5~21.5 | 0.10~0.60 | 1.50~3.50 | 1 | 0.05~0.20 | / | / | D2d |
| 4362-323-04-I | 0.03 | 1 | 2 | 0.035 | 0.015 | 22.0~24.5 | 0.10~0.60 | 3.5~5.5 | 0.10~0.60 | 0.05~0.20 | / | / | D2d |
| 4062-322-02-U | 0.03 | 1 | 2 | 0.04 | 0.01 | 21.5~24.0 | 0.45 | 1.00~2.90 | / | 0.16~0.28 | / | / | D4 |
| 4162-321-01-E | 0.04 | 1 | 4.0~6.0 | 0.04 | 0.015 | 21.0~22.0 | 0.10~0.80 | 1.35~1.90 | 0.10~0.80 | 0.20~0.25 | / | / | D4 |
| 4662-824-41-X | 0.03 | 0.7 | 2.50~4.0 | 0.035 | 0.005 | 23.0~25.0 | 1.00~2.00 | 3.0~4.5 | 0.10~0.80 | 0.20~0.30 | / | / | D4 |
| 4462-318-03-I | 0.03 | 1 | 2 | 0.035 | 0.015 | 21.0~23.0 | 2.5~3.5 | 4.5~6.5 | / | 0.10~0.22 | / | / | D6 |
| 4481-312-60-J | 0.03 | 1 | 1.5 | 0.04 | 0.03 | 24.0~26.0 | 2.5~3.5 | 5.5~7.5 | / | 0.08~0.30 | / | / | D6 |
| 4410-327-50-E | 0.03 | 1 | 2 | 0.035 | 0.015 | 24.0~26.0 | 3.0~4.5 | 6.0~8.0 | / | 0.24~0.35 | / | / | D8 |
| 4501-327-60-I c | 0.03 | 1 | 1 | 0.03 | 0.01 | 24.0~26.0 | 3.0~4.0 | 6.0~8.0 | 0.5~1.0 | 0.20~0.30 | / | / | D8 |
| 4507-325-20-I | 0.03 | 0.7 | 2 | 0.035 | 0.015 | 24.0~26.0 | 3.0~4.0 | 6.0~8.0 | 1.0~2.5 | 0.20~0.30 | / | / | D8 |
| 注：表中所列成分除标明范围或最小值外，其余均为最大值。 | |||||||||||||
| a 未经买方同意，不宜将未规定的元素加入钢材中，除非为了完成冶炼。应采取一切合理的预防措施，以防止从制造中使用的废料或其他材料中添加影响淬透性、机械性能和适用性的元素。 | |||||||||||||
| b 钢的组别与GB/T 3098.6和GB/T 3098.15规定的成分范围最接近，但是，本表中包含的不一定完全符合。 | |||||||||||||
| c 钨的含量应为0.5%~1.0%。 | |||||||||||||
| d 当wCr＋3.3wMo＋16wN＞24和符合GB/T 3098不锈钢系列标准时，可被认同为D4。 | |||||||||||||